The Department of Energy is seeking ancillary technologies to enhance the performance of high filed superconducting materials critical for the very high-field magnets to be used in a future particle accelerator. Bi-2212 round wire, a high temperature superconductor, is one of the best candidates for this purpose. This composite consists of many ...

Phase 1 SBIR

Agency: Department of Energy
Topic: 64 C-2011
Budget: 01/01/11 - 12/31/11

The typical critical current density of best Nb3Sn superconducting composite is approximately 1600 A/mm2 at 15T and 4.2K. This density is achieved in RRP strand with ternary alloy of either (Nb, Ti)3Sn or (Nb,Ta)3Sn. This objective of this study is to improve superconducting property of (Nb,Ta,Ti)3Sn to Jc & gt1800 A/mm2 at the same field and te...

Phase 1 SBIR

Agency: Department of Energy
Topic: 62 A-2010
Budget: 01/01/10 - 12/31/10

The Department of Energy is seeking superconducting material for a very high-field magnet to be used in a future particle accelerator. Bi-2212 round wire, a high temperature superconductor, is one of the best candidates for this purpose. However, there are significant amount of pores present in the filament packed with powder. These pores are li...

Phase 1 SBIR

Agency: Department of Energy
Topic: 2009
Budget: 01/01/09 - 12/31/09

The typical critical current density of best Nb3Sn superconducting composite is approximately 1600 A/mm2 at 15T and 4.2K. This density is achieved in RRP® strand with ternary alloy of either (Nb,Ti)3Sn or (Nb,Ta)3Sn. This objective of this study is to improve superconducting property of (Nb, Ta, Ti)3Sn to Jc >1800 A/mm2 at the same field and tem...